Hot Dip Galvanized Angle Steel

Hot dip galvanized angle steel is also known as hot-dip galvanized angle steel or hot-dip galvanized angle steel. It is to immerse the derusted angle steel in a molten zinc solution at around 500 ℃, so that a zinc layer is attached to the surface of the angle steel, thus achieving the purpose of corrosion prevention. It is suitable for various strong corrosive environments such as acid and alkali mist.
Process: Hot dip galvanized angle steel Process: Angle steel pickling → water washing → immersion in auxiliary plating solvent → drying preheating → hanging plating → cooling → passivation → cleaning → polishing → completion of hot dip galvanizing.
The galvanized layer thickness of hot-dip galvanized angle steel is uniform, up to 30-50um, with good reliability. The galvanized layer is metallurgical bonded with the steel, becoming a part of the steel surface. Therefore, the coating durability of hot-dip galvanized angle steel is relatively reliable. The raw material of hot-dip galvanized angle steel is angle steel, so it is classified as the same as angle steel.